DETAILS
LINCORE® 96-S ideal for work rolls and backup rolls applications when water spray causes pitting on tool steel deposits to be used with recommended Lincoln weld® 801 and Lincoln weld® 802 standard flux for semiautomatic operations.
Features
- Metal-cored wire which produces a high carbon, 420 stainless steel deposit
- Use where a higher hardness is required
- Can be used on work rolls and backup rolls when water spray causes pitting on tool steel deposits
Typical Applications
- Steel Industry
- Caster rolls
Welding Positions
- Flat/Horizontal
Service Information
You May Also Need
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
MECHANICAL PROPERTIES
| Flux | Classification | Hardness Rockwell C |
|---|---|---|
| Lincolnweld® 801® | Typical Result | 48-54 |
DEPOSIT COMPOSITION
| Flux | Classification | %C | %Cr | %Mn | %Si |
|---|---|---|---|---|---|
| Lincolnweld® 801® | Typical Result | 0.23 | 13.0 | 1.2 | 0.4 |
TYPICAL OPERATING PROCEDURES
| Diameter | Polarity |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
|---|---|---|---|---|
| 3/32 in (2.4 mm) | DC+ | 1.7 (65) | 24 | 250 |
| 3/32 in (2.4 mm) | DC+ | 2.5 (100) | 28 | 525 |
| 3/32 in (2.4 mm) | DC+ | 4.4 (175) | 31 | 450 |
| 1/8 in (3.2 mm) | DC+ | 1.5 (60) | 26 | 360 |
| 1/8 in (3.2 mm) | DC+ | 2.5 (100) | 28 | 525 |
| 1/8 in (3.2 mm) | DC+ | 3.6 (140) | 30 | 635 |
| 5/32 in (4.0 mm) | DC+ | 1.4 (55) | 27 | 450 |
| 5/32 in (4.0 mm) | DC+ | 2.2 (85) | 30 | 650 |
| 5/32 in (4.0 mm) | DC+ | 2.9 (115) | 32 | 775 |