Détails
LINCOLNWELD® 316/316L has a 2-3% molybdenum content which improves pitting corrosion resistance of the weld deposit, while the low carbon content reduces the possibility of carbide precipitation and intergranular corrosion.
Traits
- Designed to be used primarily with basic fluxes that recover nearly all of the wire chromium in the deposit
- Low carbon content recommended where there is a risk of intergranular corrosion
- The 2-3% molybdenum improves pitting corrosion resistance of the weld deposit
- Low carbon content reduces the possibility of carbide precipitation and intergranular corrosion
Applications typiques
- ASTM A743, A744 Types CF-8 and CF-3
- Developed for welding type 316 and 316L stainless steels
- For joining the more common austenitic stainless steel grades referred to as “18-8” steels
- For very good corrosion resistance in acid environments
- Power Generation
Positions de soudage
- Not applicable
Gaz de protection
- N/A
Disclaimers
Des informations de service
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
CONFORMANCE
| CONFORMANCES | SPECIFICATION | CLASSIFICATION |
|---|---|---|
| AWS | AWS A5.9 | ER316, ER316L |
| ISO | ISO 14343-B | SS316L |
| ABS | AWS A5.9 | ER316, ER316L |
| CWB | CSA W48 | ER316, ER316L |
| MIL | MIL-E-19933E AMD1 | MIL-316L |
| CONFORMANCES | SPECIFICATION | CLASSIFICATION |
|---|---|---|
| AWS | AWS A5.9 | ER316, ER316L |
| ISO | ISO 14343-B | SS316L |
| ABS | AWS A5.9 | ER316, ER316L |
| CWB | CSA W48 | ER316, ER316L |
| MIL | MIL-E-19933E AMD1 | MIL-316L |
MECHANICAL PROPERTIES
| Flux | Classification |
Yield Strength @ 0.2% Offset
MPa (ksi) |
Tensile Strength
MPa (ksi) |
Elongation
% |
|---|---|---|---|---|
| Lincolnweld® P2007™ | Typical Result | 390 (57) | 559 (81) | 39 |
| Flux | Classification |
Yield Strength @ 0.2% Offset
MPa (ksi) |
Tensile Strength
MPa (ksi) |
Elongation
% |
|---|---|---|---|---|
| Lincolnweld® P2007™ | Typical Result | 390 (57) | 559 (81) | 39 |
WIRE COMPOSITION
| Classification | %C | %Cr | %Cu | %Mn | %Mo | %N | %Nb | %Ni | %P | %S | %Si | Ferrite Number (Delong ©) | Ferrite Number (WRC-1992 ©) |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| ER316L Requirement | 0.03 max. | 18.0 - 20.0 | 0.75 max. | 1.0 - 2.5 | 2.0 - 3.0 | Info. Only | Info. Only | 11.0 - 14.0 | 0.03 max. | 0.03 max. | 0.30 - 0.65 | Info. Only | Info. Only |
| Typical Result | 0.01-0.02 | 18.5-19.1 | 0.03-0.13 | 1.4-1.8 | 2.2-2.6 | 0.03-0.04 | 0.01 max. | 11.8-12.3 | 0.02 | 0.01 max. | 0.32-0.40 | 8-12 | 7-11 |
| Classification | %C | %Cr | %Cu | %Mn | %Mo | %N | %Nb | %Ni | %P | %S | %Si | Ferrite Number (Delong ©) | Ferrite Number (WRC-1992 ©) |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| ER316L Requirement | 0.03 max. | 18.0 - 20.0 | 0.75 max. | 1.0 - 2.5 | 2.0 - 3.0 | Info. Only | Info. Only | 11.0 - 14.0 | 0.03 max. | 0.03 max. | 0.30 - 0.65 | Info. Only | Info. Only |
| Typical Result | 0.01-0.02 | 18.5-19.1 | 0.03-0.13 | 1.4-1.8 | 2.2-2.6 | 0.03-0.04 | 0.01 max. | 11.8-12.3 | 0.02 | 0.01 max. | 0.32-0.40 | 8-12 | 7-11 |
TYPICAL OPERATING PROCEDURES
| Diameter |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
|---|---|---|---|
| 5/64 in (2.0 mm) | 2.0-6.1 (80-240) | 24-30 | 190-500 |
| 3/32 in (2.4 mm) | 1.5-5.3 (60-210) | 26-32 | 195-575 |
| 1/8 in (3.2 mm) | 0.9-2.8 (35-110) | 28-34 | 200-700 |
| 5/32 in (4.0 mm) | 0.8-1.9 (30-75) | 30-36 | 320-775 |
| Diameter |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
|---|---|---|---|
| 5/64 in (2.0 mm) | 2.0-6.1 (80-240) | 24-30 | 190-500 |
| 3/32 in (2.4 mm) | 1.5-5.3 (60-210) | 26-32 | 195-575 |
| 1/8 in (3.2 mm) | 0.9-2.8 (35-110) | 28-34 | 200-700 |
| 5/32 in (4.0 mm) | 0.8-1.9 (30-75) | 30-36 | 320-775 |