Lincore® 15CrMn

Flux-Cored Self-Shielded (FCAW-S)

CLASSIFICATIONS:
EN ISO : T Fe9

LINCORE® 15CRMN Wire for spreader cones, crusher hammers, and manganese parts. Use as a build-up layer before capping with abrasion-resistant alloys.

Diameter

Select Diameter

  • 2.0 mm
  • 2.8 mm

Package

Select Package

  • 11.3 KG SPOOL
  • 22.7 KG COIL

DETAILS

LINCORE® 15CRMN provides an austenitic manganese deposit which exhibits very good crack resistance ideal for open arc mode for joining austenitic manganese steel to carbon steel, low alloy steel, austenitic manganese steel, or stainless steel offers unlimited layers with proper preheat and interpass temperatures and procedures.

Features

  • Provides an austenitic manganese deposit which exhibits very good crack resistance
  • Work-hardens for overlay or joining austenitic manganese steel to itself or to carbon steel
  • Can be used as a build-up layer before capping with abrasion resistant alloys
  • Unlimited layers with proper preheat and interpass temperatures and procedures

Typical Applications

  • Spreader cones
  • Crusher hammers
  • Austenitic manganese parts

Welding Positions

  • Flat/Horizontal

Service Information

You May Also Need

K126 Classic 350A FCAW-SS

K126® Classic® Innershield® 350A FCAW-SS Welding Gun 10 ft 062-332

K126-1
Drive Roll Kit, Solid Wire

Drive roll kit (4R) 2.8 mm, hardfacing

KP1505-7/64H
50lb Coil Ultracore 70C

Lincore® 15CrMn

ED022061

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

MECHANICAL PROPERTIES

Classification Hardness Rockwell C
Typical Result 18-22
Typical Result, Work-hardened 45-50

DEPOSIT COMPOSITION

Classification %C %Cr %Mn %Si
Typical Result 0.4 16.0 15.0 0.2

TYPICAL OPERATING PROCEDURES

Diameter Polarity ESO
mm (in.) 		Wire Feed Speed
m/min (in/min) 		Voltage
volts 		Approx. Current
amps 		Deposition Rate
kg/hr (lb/hr)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 3.2 (125) 26 210 3.3 (7.3)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 5.1 (200) 29 280 5.3 (11.7)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 6.4 (250) 30 320 6.8 (15.1)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 8.9 (350) 32 380 9.7 (21.3)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 1.9 (75) 26 250 2.5 (5.5)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.2 (125) 28 320 5.1 (11.3)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.8 (150) 29 350 6.6 (14.6)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 4.4 (175) 30 380 7.5 (16.4)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 3.8 (150) 30 320 6.7 (14.9)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 5.1 (200) 33 390 8.7 (19.2)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 5.7 (225) 34 410 9.8 (21.7)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 6.4 (250) 35 425 11.4 (25.1)

NOTES

Note
As with all austenitic manganese welding products, interpass temperatures should be limited to 260°C (500°F) maximum.
A stringer bead, or at most, a slight weave is recommended to limit heat build-up. Excessive heat build-up causes manganese carbide precipitation that damages the toughness of austenitic manganese.