Sarma tubulara cu pulberi cu auto-protectie (FCAW-S)

CLASIFICARI:
EN ISO : T Fe9

LINCORE® 15CRMN Wire for spreader cones, crusher hammers, and manganese parts. Use as a build-up layer before capping with abrasion-resistant alloys.

Diametru

Selectare diametru

  • 2,8 mm
  • 2.0 mm

Ambalaj

Selectare ambalaj

  • 11.3 KG SPOOL
  • 22.7 KG COIL

DETALII

LINCORE® 15CRMN provides an austenitic manganese deposit which exhibits very good crack resistance ideal for open arc mode for joining austenitic manganese steel to carbon steel, low alloy steel, austenitic manganese steel, or stainless steel offers unlimited layers with proper preheat and interpass temperatures and procedures.

Caracteristici

  • Poate fi utilizata cu arc descoperit pentru imbinarile dintre otel manganos cu otel carbon, otel slab aliat, austenitic sau otel inoxidabil
  • Straturi nelimitate, cu proceduri adecvate pentru temperaturile de preincalzire si intre straturi
  • Poate fi folosit ca strat tampon inainte de placarea cu consumabile cu rezistenta la abraziune
  • Unlimited layers with proper preheat and interpass temperatures and procedures

Aplicații tipice

  • Bara, Galeata, Zdrobitor, Lame
  • Tragator, Draga, Ciocan, Mixer / Amestecator
  • Vetre deschise, Placi, Generatoare de energie, Pompe, Cai de rulare
  • Role, Ecrane, Lopeti, Dinti, Roti

Poziții de sudare

  • La masa / Orizontal

Informații despre service

Documentație

S-ar putea să aveți nevoie și de

K126 Classic 350A FCAW-SS

Pistol de sudare K126® Classic® Innershield® 350A FCAW-SS 10 ft 062-332

K126-1
50lb Coil Ultracore 70C

Lincore® 15CrMn

ED022061

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. Pagina de căutare FDS

MECHANICAL PROPERTIES

Classification Hardness Rockwell C
Typical Result 18-22
Typical Result, Work-hardened 45-50

DEPOSIT COMPOSITION

Classification %C %Cr %Mn %Si
Typical Result 0.4 16.0 15.0 0.2

TYPICAL OPERATING PROCEDURES

Diameter Polarity ESO
mm (in.) 		Wire Feed Speed
m/min (in/min) 		Voltage
volts 		Approx. Current
amps 		Deposition Rate
kg/hr (lb/hr)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 3.2 (125) 26 210 3.3 (7.3)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 5.1 (200) 29 280 5.3 (11.7)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 6.4 (250) 30 320 6.8 (15.1)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 8.9 (350) 32 380 9.7 (21.3)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 1.9 (75) 26 250 2.5 (5.5)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.2 (125) 28 320 5.1 (11.3)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.8 (150) 29 350 6.6 (14.6)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 4.4 (175) 30 380 7.5 (16.4)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 3.8 (150) 30 320 6.7 (14.9)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 5.1 (200) 33 390 8.7 (19.2)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 5.7 (225) 34 410 9.8 (21.7)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 6.4 (250) 35 425 11.4 (25.1)

NOTES

Note
As with all austenitic manganese welding products, interpass temperatures should be limited to 260°C (500°F) maximum.
A stringer bead, or at most, a slight weave is recommended to limit heat build-up. Excessive heat build-up causes manganese carbide precipitation that damages the toughness of austenitic manganese.