Lincore® 60-O

Sarma tubulara cu pulberi cu auto-protectie (FCAW-S)

LINCORE® 60-O Wire designed for bucket lips, crusher hammers, dozer blades, and ripper teeth applications.

Diametru

Selectare diametru

  • 1,1 mm
  • 1,6 mm
  • 2,0 mm

Ambalaj

Selectare ambalaj

  • 11.3 KG SPOOL
  • 22.7 KG COIL

DETALII

LINCORE® 60-O ideal for carbon, low alloy, manganese, stainless steels and cast iron to be used at temperatures up to 704°C (1300°F) deposits feature higher alloy levels than to resist both abrasion and moderate impact limited to two layers with a Rockwell Hardness range of 55-60 (RHC) during sever abrasion.

Caracteristici

  • Pentru a fi utiliza pe otel carbon, slab aliat, manganos si otel inoxidabil si fonta
  • Depunerile sunt limitate la doua treceri
  • Depunerile prezinta niveluri mai mari de elemente de aliere ca sa reziste atat la abraziune si la impact moderat
  • Deposit is limited to two layers

Aplicații tipice

  • Buza galeata
  • Ciocan de concasor
  • Jgheaburi minereuri
  • Lame de buldozer
  • Dinti excavare

Poziții de sudare

  • La masa / Orizontal

Informații despre service

Documentație

S-ar putea să aveți nevoie și de

33 lb Steel Spool Outershield MC-409 Flux-Cored Wire

Lincore® 60-O

ED031132
50lb Coil Ultracore 70C

Lincore® 60-O

ED019887

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. Pagina de căutare FDS

MECHANICAL PROPERTIES

Classification Number of layer Hardness Rockwell C Mass Loss (G65)
Typical Result 1 Layer 50-55 0.67
Typical Result 2 Layers 55-58 0.20

DEPOSIT COMPOSITION

Classification Number of layer %Al %C %Cr %Mn %Si
Typical Result 2 Layers 0.3-0.4 4.0-4.6 18.5-22.9 1.0-1.8 0.5-0.9

TYPICAL OPERATING PROCEDURES

Diameter Polarity ESO
mm (in.) 		Wire Feed Speed
m/min (in/min) 		Voltage
volts 		Approx. Current
amps 		Deposition Rate
kg/hr (lb/hr)
.045" (1.1 mm) DC+ 19 (1) 5.1 (200) 21 125 1.9 (4.1)
.045" (1.1 mm) DC+ 19 (1) 10.2 (400) 25 185 3.7 (8.2)
.045" (1.1 mm) DC+ 19 (1) 12.7 (500) 27 210 4.7 (10.3)
1/16" (1.6 mm) DC+ 22 (1) 5.1 (200) 28 240 3.4 (7.6)
1/16" (1.6 mm) DC+ 22 (1) 7.6 (300) 31 300 5.1 (11.2)
1/16" (1.6 mm) DC+ 22 (1) 11.4 (450) 33 350 7.5 (16.6)
5/64" (2.0 mm) DC+ 32 (1) 3.2 (125) 26 250 3.4 (7.4)
5/64" (2.0 mm) DC+ 32 (1) 5.1 (200) 30 350 5.4 (12.0)
5/64" (2.0 mm) DC+ 32 (1) 6.4 (250) 32 400 6.8 (15.1)
7/64" (2.8 mm) DC+ 29 (1) 1.9 (75) 27 250 3.4 (7.4)
7/64" (2.8 mm) DC+ 29 (1) 3.2 (125) 30 340 5.4 (11.9)
7/64" (2.8 mm) DC+ 29 (1) 4.4 (175) 32 420 7.5 (16.5)

NOTES

Note
Deposit thickness limit is two layers unless high travel speed is used to obtain very closely spaced check cracks. Many layers can be used with high travel speed and small bead sizes to ensure close-spaced check cracks.
Lincore® 60-O deposit cross cracks (commonly called cross-checking) on cooling. This is desirable, since cross-cracking of the deposit relieves cooling stresses and prevents spalling.