Diametre / Ambalaj
|
Diametre |
11.3 KG SPOOL |
|---|---|
| 1,6 mm | ED031134 |
DETALII
LINCORE® T & D ideal for build-up of tool steel dies and edges, or applying wear resistance surface on carbon and low alloy steels delivers a deposit similar to H12 tool steel with a Rockwell Hardness range of 48- 55(HRC) to produces a crack-free wear resistant tool steel.
Caracteristici
- Ofera un metal depus similar cu cel al otelului de scule H12
- Pentru realizarea matritelor si incarcarea marginilor sau pentru incarcarea dura a suprafetelor din otel carbon si slab aliat pentru a rezistente la uzura
- A fi utilizat pe otel carbon, slab aliat si otel de scule
Aplicații tipice
- Dornuri de matritare, Cai de rulare, Mori, Discuri / Tambur, Bara, Pulverizator, Galeata, Macara
- Lame de forfecare, Dinti, Tragator / Galeata / Dinti, Pinion de antrenare, Extrudor, Roti dintate, Roti de rulare, Cuptor, Echipamente de minerit / Roata
- Extractor, Lopeti cu galeti, Hartie/ Pasta, Pompa, Scarificator /Dinti, Melc, Generatoare de putere, Tractor
Poziții de sudare
- La masa / Orizontal
Informații despre service
Documentație
S-ar putea să aveți nevoie și de
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. Pagina de căutare FDS
MECHANICAL PROPERTIES
| Classification | Hardness Rockwell C |
|---|---|
| Typical Result | 48-55 |
| Typical Result, Tempered | 55-65 |
DEPOSIT COMPOSITION
| Classification | %Al | %C | %Cr | %Mn | %Mo | %Si | %W |
|---|---|---|---|---|---|---|---|
| Typical Result | 1.8 | 0.65 | 7.0 | 1.5 | 1.4 | 0.8 | 1.6 |
TYPICAL OPERATING PROCEDURES
| Diameter | Polarity |
ESO
mm (in.) |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
Deposition Rate
kg/hr (lb/hr) |
|---|---|---|---|---|---|---|
| 1/16 in (1.6 mm) | DC+ | 32 (1 1/4) | 3.8 (150) | 22 | 170 | 2.4 (5.4) |
| 1/16 in (1.6 mm) | DC+ | 32 (1 1/4) | 5.1 (200) | 23 | 210 | 3.6 (7.9) |
| 1/16 in (1.6 mm) | DC+ | 32 (1 1/4) | 6.4 (250) | 24 | 250 | 4.1 (8.9) |
| 1/16 in (1.6 mm) | DC+ | 32 (1 1/4) | 7.6 (300) | 25 | 270 | 4.9 (10.8) |
| 1/16 in (1.6 mm) | DC+ | 32 (1 1/4) | 8.9 (350) | 26 | 300 | 5.4 (12.0) |
NOTES
| Note |
|---|
| Minimum preheat and interpass temperatures of 315°C (600°F) are essential for crack-free welding on mild steel or low alloy steel. For crack-free welding on tool steel parts, preheat of 538°C (1000°F) or higher may be necessary. |
| After welding, very slow cooling to 121°C (250°F) is usually required. This can be followed by post-weld heat treating at 538° - 593°C (1000° - 1100°F) to develop maximum hardness |