Lincolnweld® 960®

Çaplar	22,7 KG PE BAG
FLUX	ED038167

DETAYLAR

General purpose flux designed for butt and fillet welds joints, in both single and multiple pass techniques. Recommended for automatic and semi-automatic submerged arc welding. A versatile, cost-effective flux that can be used with many alloy systems.

Özellikleri

Versatile flux
High current carrying capacity
For both single -run and multi-run techniques with moderate weld metal properties requirements
Can be used on weathering steels when combined with Lincolnweld® LA-75
Actual (Type 3.1) certificates for each lot of flux showing chemical composition, particle size and moisture level are available in the certificate center of lincolnelectric.com
Q2 lot testing with mechanical results for ED030841
Mild Steel Lincolnweld® L-50®, L-61®, LA-71 Low Alloy Steel Lincolnweld® LA-75, LA-85, LA-93, LA-100

Tipik Uygulamalar

Single and multiple pass welding
Fillet and butt welds with unlimited plate thickness
Can weld steel with heavy scale or rust when used with Lincolnweld® L-50® wire

Özel Özellikler

Basicity Index: 1.1 Density: 1.4 g/cm

Servis Bilgileri

Belgeler

Submerged Arc Guide

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Arama sayfası

Test sonucunu görün sorumluluk reddi

MECHANICAL PROPERTIES

Wire	Classification	Postweld Heat Treatment	Yield Strength @ 0.2% Offset MPa (ksi)	Tensile Strength MPa (ksi)	Elongation %	Charpy V-Notch J (ft-lbs) @ -30°C (-20°F)	Charpy V-Notch J (ft-lbs) @ -40°C (-40°F)	Charpy V-Notch J (ft-lbs) @ -45°C (-50°F)	Charpy V-Notch J (ft-lbs) @ -50°C (-60°F)
Lincolnweld® L-50®	F7A2-EM13K-H4	As-welded	410 (59)	510 (74)	32	47 (35)
Lincolnweld® L-56®	F7A2-EH11K-H4	As-welded	480 (69)	590 (86)	29	42 (31)
Lincolnweld® L-61®	F6P4-EM12K	1 hour @ 620°C (1150°F)	340 (49)	460 (67)	35		140 (103)
Lincolnweld® L-61®	F7A2-EM12K-H8	As-welded	410 (59)	500 (72)	31	152 (112)
Lincolnweld® LA-100	F10A4-EM2-G-H4	As-welded	650 (94)	720 (105)	23		50 (37)
Lincolnweld® LA-71	F7A2-EM14K-H4	As-welded	460 (67)	570 (82)	29	68 (50)
Lincolnweld® LA-71	F7P2-EM14K-H4	1 hour @ 620°C (1150°F)	410 (60)	540 (79)	30	94 (69)
Lincolnweld® LA-75	F7P6-ENi1K-Ni1-H4	1 hour @ 620°C (1150°F)	440 (64)	560 (81)	29				56 (41)
Lincolnweld® LA-75	F8A2-ENi1K-Ni1-H4	As-welded	480 (70)	580 (84)	25	81 (60)
Lincolnweld® LA-85 (LNS 165)	F7P5-ENi5-G-H4	1 hour @ 620°C (1150°F)	470 (68)	570 (83)	27			58 (43)
Lincolnweld® LA-85 (LNS 165)	F8A2-ENi5-G-H4	As-welded	500 (72)	590 (86)	26	68 (50)
Lincolnweld® LA-93 (LNS 151)	F9P0-EB3-G-H8	1 hour @ 690°C (1275°F)	540 (79)	650 (94)	23

DEPOSIT COMPOSITION

Wire	Classification	%Ti	%C	%Cr	%Cu	%Mn	%Mo	%Ni	%P	%S	%Si	%Ti+V+Zr	Diffusible Hydrogen mL/100g Weld Metal
Lincolnweld® L-50®	F7A2-EM13K-H4		0.06		0.09	1.48			0.016	0.008	0.58		4
Lincolnweld® L-56®	F7A2-EH11K-H4		0.05		0.11	1.86			0.016	0.006	0.96		4
Lincolnweld® L-61®	F6P4-EM12K		0.05		0.10	1.30			0.021	0.004	0.38
Lincolnweld® L-61®	F7A2-EM12K-H8		0.05		0.06	1.27			0.015	0.009	0.42		5
Lincolnweld® LA-100	F10A4-EM2-G-H4	0.04	0.05	0.03	0.14	1.63	0.44	1.96	0.008	0.004	0.45	0.04	3
Lincolnweld® LA-71	F7A2-EM14K-H4	0.02	0.06		0.15	1.58			0.015	0.010	0.69		4
Lincolnweld® LA-71	F7P2-EM14K-H4	0.02	0.07		0.15	1.58			0.015	0.010	0.69		4
Lincolnweld® LA-75	F7P6-ENi1K-Ni1-H4		0.04	0.04	0.11	1.57	0.01	0.85	0.014	0.009	0.73	0.01	3
Lincolnweld® LA-75	F8A2-ENi1K-Ni1-H4		0.05	0.04	0.11	1.54	0.01	0.84	0.014	0.010	0.71	0.01	3
Lincolnweld® LA-85 (LNS 165)	F7P5-ENi5-G-H4		0.05	0.03	0.09	1.61	0.22	0.85	0.016	0.010	0.42		4
Lincolnweld® LA-85 (LNS 165)	F8A2-ENi5-G-H4		0.05	0.03	0.08	1.62	0.23	0.85	0.016	0.010	0.42		4
Lincolnweld® LA-93 (LNS 151)	F9P0-EB3-G-H8		0.05	2.10	0.08	1.17	0.94		0.014	0.007	0.32		3

FLUX COMPOSITION

Classification	%Al2O3	%CaF2	%CaO	%MgO	%MnO	%Na2O	%SiO2	%TiO2	%Metal Alloys
Typical Result	29	11	1	22	10	2	21	1	3