Cardboard box SAF-FRO for filler metal packaging

Diameters / Packaging

Diameters
 Carton box 19.5 KG (3 x 6.5 KG, approx. 285 pcs)
4.0x450 mm W000258787

SAFMANGA

Stick (SMAW) | W000258787

CLASSIFICATIONS:
EN 14700 : ~E Fe9 (Nearest classification)
DIN 8555 : E 7-UM-200 KP

Stick electrode SAFMANGA - 4.0x450 mm - Carton box 19.5 KG (approx. 285 pcs)

Diameter

Select Diameter

  • 4.0x450 mm

Package

Select Package

  • Carton box 19.5 KG (3 x 6.5 KG, approx. 285 pcs)

DETAILS

SAFMANGA is a basic coated austenitic manganese steel MMA electrode for wear resisting hard facing deposits. Used for hardfacing or buttering on carbon steels and high Mn steels, the deposit is only machinable by grinding. The weld metal will increase in hardness by cold-working, from~ 200-250 HB to ~400-500 HB, therefore it is particularly suitable for components which are subjected mainly to wear, caused by heavy impact and shock. During welding, the work pieces should not become too hot and if necessary should be allowed to cool down. When welding large work pieces of austenitic manganese steel, such as crusher jaw plates, it is advisable to weld in a water bath.

Features

  • SAFMANGA is a basic coated austenitic manganese steel MMA electrode for wear resisting hard facing deposits. Used for hardfacing or buttering on carbon steels and high Mn steels, the deposit is only machinable by grinding. The weld metal will increase in hardness by cold-working, from~ 200-250 HB to ~400-500 HB, therefore it is particularly suitable for components which are subjected mainly to wear, caused by heavy impact and shock. During welding, the work pieces should not become too hot and if necessary should be allowed to cool down. When welding large work pieces of austenitic manganese steel, such as crusher jaw plates, it is advisable to weld in a water bath.
  • Flat welding position only.
  • Shall be used in DC+ current

Service Information