Innershield® NR®-212

Flux-Cored Self-Shielded (FCAW-S) | ED026858

AWS:
E71TG-G-H16
E71TG-AZ-G-H16

Innershield® NR®-212 from Lincoln Electric is recommended for single or multiple pass welding on up to 19 mm (3/4 in.) thicknesses.

Diameter

Select Diameter

  • 0.045 in (1.1 mm)
  • 0.068 in (1.7 mm)
  • 5/64 in (2.0 mm)

Package

Select Package

  • (4) 14 lb Coil
  • 25 lb Spool
  • 50 lb Coil
Buy Now

DETAILS

Designed with the same arc characteristics of NR®-211-MP, but for use on a larger range of applications. Recommended for single or multiple pass welding on up to 19 mm (3/4 in) thicknesses.

Features

  • Accommodates a wide range of mild steels
  • Fast freeze characteristics accommodate poor fit-up
  • Smooth arc performance
  • Ease of use

Disclaimers

Warning -

Cancer and Reproductive Harm -

www.P65Warnings.ca.gov

Service Information

Documentation

You May Also Need

K126 Classic 350A FCAW-SS

K126® Classic® Innershield® 350A FCAW-SS Welding Gun 15 ft 062-332

K126-2
Innershield Flux Cored wire, 25 or 30 lb steel spool

Innershield® NR®-212 Flux-Cored (FCAW-S) Wire

ED030646
Gun Receiver Bushing

Gun Receiver Bushing for Lincoln Electric® Guns

K1500-1
Drive Roll and Guide Tube Kit

Drive Roll Kit 5/64 in (2.0 mm) Solid/Cored Wire

KP1697-5/64
View All

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

See test result disclaimer

CONFORMANCE

CONFORMANCES SPECIFICATION CLASSIFICATION
AWS AWS A5.29 E71TG-G-H16
AWS AWS A5.36 E71TG-AZ-G-H16
CWB CSA W48 E491TG-AZ-G-H16 (E491TG-G-H16)

MECHANICAL PROPERTIES

Classification Polarity Yield Strength @ 0.2% Offset
MPa (ksi) 		Tensile Strength
MPa (ksi) 		Elongation
%
E71TG-G-H16 Requirement Not Specified 400 (58) min. 480-620 (70-90) 20 min.
Typical Result, As-welded DC- 410 (60) 540-610 (78-89) 22

DEPOSIT COMPOSITION

Classification Polarity %Al %C %Mn %Mo %Ni %P %S %Si %V Diffusible Hydrogen
mL/100g Weld Metal
E71TG-G-H16 Requirement Not Specified 1.8 max. 0.50 min. * 0.20 min. * 0.50 min. * 0.030 max. 0.030 max. 1.00 max. 0.10 min. * 16.0 max.
Typical Result DC- 1.2-1.8 0.11 0.86-1.99 0.02 0.88-1.21 0.013 0.005 0.15-0.34 0.005 6.1

TYPICAL OPERATING PROCEDURES

Diameter Polarity CTWD
mm (in.) 		Wire Feed Speed
m/min (in/min) 		Voltage
volts 		Approx. Current
amps 		Melt-off Rate
kg/hr (lb/hr) 		Deposition Rate
kg/hr (lb/hr) 		Efficiency
%
0.045 in (1.1 mm) DC- 16 (5/8) 1.4 (55) 14-15 75 0.5 (1.3) 0.5 (1.1) 84
0.045 in (1.1 mm) DC- 16 (5/8) 1.8 (70) 15-16 90 0.7 (1.6) 0.6 (1.4) 87
0.045 in (1.1 mm) DC- 16 (5/8) 2.3 (90) 16-17 115 1.0 (2.1) 0.8 (1.8) 85
0.045 in (1.1 mm) DC- 16 (5/8) 2.8 (110) 17-18 135 1.2 (2.6) 1.0 (2.2) 84
0.045 in (1.1 mm) DC- 16 (5/8) 3.3 (130) 18-19 155 1.4 (3.1) 1.2 (2.6) 83
0.045 in (1.1 mm) DC- 16 (5/8) 4.1 (160) 19-20 170 1.6 (3.5) 1.4 (3.0) 85
0.068 in (1.7 mm) DC- 25 (1) 1.5 (60) 16-17 145 1.4 (3.1) 1.1 (2.4) 77
0.068 in (1.7 mm) DC- 25 (1) 1.9 (75) 17-18 180 1.7 (3.8) 1.4 (3.2) 84
0.068 in (1.7 mm) DC- 25 (1) 2.3 (90) 18-19 200 2.0 (4.5) 1.7 (3.8) 84
0.068 in (1.7 mm) DC- 25 (1) 3.0 (120) 19-20 230 2.7 (6.0) 2.3 (5.2) 86
0.068 in (1.7 mm) DC- 25 (1) 3.8 (150) 20-21 255 3.3 (7.4) 2.9 (6.4) 86
0.068 in (1.7 mm) DC- 25 (1) 4.4 (175) 22-23 275 3.9 (8.7) 3.4 (7.5) 86
5/64 in (2.0 mm) DC- 25 (1) 1.5 (60) 16-17 200 1.7 (3.8) 1.5 (3.3) 86
5/64 in (2.0 mm) DC- 25 (1) 1.9 (75) 18-19 225 2.1 (4.7) 1.8 (4.1) 87
5/64 in (2.0 mm) DC- 25 (1) 2.3 (90) 19-20 245 2.6 (5.7) 2.3 (5.0) 87
5/64 in (2.0 mm) DC- 25 (1) 2.8 (110) 20-21 275 3.2 (7.1) 2.8 (6.2) 87
5/64 in (2.0 mm) DC- 25 (1) 3.3 (130) 21-23 300 3.7 (8.3) 3.3 (7.3) 87
5/64 in (2.0 mm) DC- 25 (1) 3.8 (150) 22-23 325 4.3 (9.6) 3.8 (8.4) 87

NOTES

Note
* To meet the requirements of a "G" classification, the chemical composition of the weld deposit must meet the minimum requirement for one or more of these elements.