DETAILS
LINCORE® 102W provides a tool steel deposit that retains hardness at high working temperatures produce chromium, molybdenum and tungsten chemical composition to be used with recommended Lincoln weld® 802 and Lincoln weld® 860 standard flux for semiautomatic operations.
Features
- Metal-cored wire which produces a tool steel deposit that retains hardness at high working temperatures
- Used for guide rolls, and work rolls
- Can also be used as the seat on blast furnace bells and hoppers
Typical Applications
- Steel Industry
- Work rolls
Welding Positions
- Flat/Horizontal
Service Information
You May Also Need
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
MECHANICAL PROPERTIES
| Flux | Classification | Hardness Rockwell C |
|---|---|---|
| Lincolnweld® 802® | Typical Result | 48-54 |
DEPOSIT COMPOSITION
| Flux | Classification | %C | %Cr | %Mn | %Mo | %Si | %V | %W |
|---|---|---|---|---|---|---|---|---|
| Lincolnweld® 802® | Typical Result | 0.28 | 6.5 | 1.5 | 1.0 | 0.4 | 0.15 | 1.0 |
TYPICAL OPERATING PROCEDURES
| Diameter | Polarity |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
|---|---|---|---|---|
| 3/32 in (2.4 mm) | DC+ | 1.7 (65) | 24 | 240 |
| 3/32 in (2.4 mm) | DC+ | 3.0 (120) | 28 | 400 |
| 3/32 in (2.4 mm) | DC+ | 4.4 (175) | 31 | 500 |
| 1/8 in (3.2 mm) | DC+ | 1.5 (60) | 26 | 390 |
| 1/8 in (3.2 mm) | DC+ | 2.5 (100) | 28 | 540 |
| 1/8 in (3.2 mm) | DC+ | 3.6 (140) | 30 | 680 |
| 5/32 in (4.0 mm) | DC+ | 1.4 (55) | 27 | 500 |
| 5/32 in (4.0 mm) | DC+ | 2.2 (85) | 30 | 685 |
| 5/32 in (4.0 mm) | DC+ | 2.9 (115) | 32 | 850 |