DETAILS
LINCORE® 102W provides a tool steel deposit that retains hardness at high working temperatures produce chromium, molybdenum and tungsten chemical composition to be used with recommended Lincoln weld® 802 and Lincoln weld® 860 standard flux for semiautomatic operations.
Features
- Work rolls
- Metal-to-metal sliding wear (where minimal or no lubrication is present)
Service Information
You May Also Need
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
MECHANICAL PROPERTIES
Flux | Classification | Hardness Rockwell C |
---|---|---|
Lincolnweld® 802® | Typical Result | 48-54 |
DEPOSIT COMPOSITION
Flux | Classification | %C | %Cr | %Mn | %Mo | %Si | %V | %W |
---|---|---|---|---|---|---|---|---|
Lincolnweld® 802® | Typical Result | 0.28 | 6.5 | 1.5 | 1.0 | 0.4 | 0.15 | 1.0 |
TYPICAL OPERATING PROCEDURES
Diameter | Polarity |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
---|---|---|---|---|
3/32 in (2.4 mm) | DC+ | 1.7 (65) | 24 | 240 |
3/32 in (2.4 mm) | DC+ | 3.0 (120) | 28 | 400 |
3/32 in (2.4 mm) | DC+ | 4.4 (175) | 31 | 500 |
1/8 in (3.2 mm) | DC+ | 1.5 (60) | 26 | 390 |
1/8 in (3.2 mm) | DC+ | 2.5 (100) | 28 | 540 |
1/8 in (3.2 mm) | DC+ | 3.6 (140) | 30 | 680 |
5/32 in (4.0 mm) | DC+ | 1.4 (55) | 27 | 500 |
5/32 in (4.0 mm) | DC+ | 2.2 (85) | 30 | 685 |
5/32 in (4.0 mm) | DC+ | 2.9 (115) | 32 | 850 |