DETAILS
LINCORE® 15CRMN provides an austenitic manganese deposit which exhibits very good crack resistance ideal for open arc mode for joining austenitic manganese steel to carbon steel, low alloy steel, austenitic manganese steel, or stainless steel offers unlimited layers with proper preheat and interpass temperatures and procedures.
Features
- Provides an austenitic manganese deposit which exhibits very good crack resistance
- Work-hardens for overlay or joining austenitic manganese steel to itself or to carbon steel
- Can be used as a build-up layer before capping with abrasion resistant alloys
- Unlimited layers with proper preheat and interpass temperatures and procedures
- Unlimited layers with proper preheat and interpass temperatures and procedures
Service Information
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
MECHANICAL PROPERTIES
| Classification | Hardness Rockwell C |
|---|---|
| Typical Result | 18-22 |
| Typical Result, Work-hardened | 45-50 |
DEPOSIT COMPOSITION
| Classification | %C | %Cr | %Mn | %Si |
|---|---|---|---|---|
| Typical Result | 0.4 | 16.0 | 15.0 | 0.2 |
TYPICAL OPERATING PROCEDURES
| Diameter | Polarity |
ESO
mm (in.) |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
Deposition Rate
kg/hr (lb/hr) |
|---|---|---|---|---|---|---|
| 5/64 in (2.0 mm) | DC+ | 32 (1 1/4) | 3.2 (125) | 26 | 210 | 3.3 (7.3) |
| 5/64 in (2.0 mm) | DC+ | 32 (1 1/4) | 5.1 (200) | 29 | 280 | 5.3 (11.7) |
| 5/64 in (2.0 mm) | DC+ | 32 (1 1/4) | 6.4 (250) | 30 | 320 | 6.8 (15.1) |
| 5/64 in (2.0 mm) | DC+ | 32 (1 1/4) | 8.9 (350) | 32 | 380 | 9.7 (21.3) |
| 7/64 in (2.8 mm) | DC+ | 45 (1 3/4) | 1.9 (75) | 26 | 250 | 2.5 (5.5) |
| 7/64 in (2.8 mm) | DC+ | 45 (1 3/4) | 3.2 (125) | 28 | 320 | 5.1 (11.3) |
| 7/64 in (2.8 mm) | DC+ | 45 (1 3/4) | 3.8 (150) | 29 | 350 | 6.6 (14.6) |
| 7/64 in (2.8 mm) | DC+ | 45 (1 3/4) | 4.4 (175) | 30 | 380 | 7.5 (16.4) |
| 7/64 in (2.8 mm) | DC+ | 64 (2 1/2) | 3.8 (150) | 30 | 320 | 6.7 (14.9) |
| 7/64 in (2.8 mm) | DC+ | 64 (2 1/2) | 5.1 (200) | 33 | 390 | 8.7 (19.2) |
| 7/64 in (2.8 mm) | DC+ | 64 (2 1/2) | 5.7 (225) | 34 | 410 | 9.8 (21.7) |
| 7/64 in (2.8 mm) | DC+ | 64 (2 1/2) | 6.4 (250) | 35 | 425 | 11.4 (25.1) |
NOTES
| Note |
|---|
| As with all austenitic manganese welding products, interpass temperatures should be limited to 260°C (500°F) maximum. |
| A stringer bead, or at most, a slight weave is recommended to limit heat build-up. Excessive heat build-up causes manganese carbide precipitation that damages the toughness of austenitic manganese. |