DETAILS
LINCORE® 410NiMo ideal for high corrosion resistance, increased hardness and toughness compared to LINCORE® 410 produces chromium, nickel and molybdenum chemical composition to be used with recommended Lincoln weld® 801, 802 and 860 standard fluxes for semiautomatic operations.
Features
- Metal-cored wire with low carbon deposit, which forms softer, tougher martensitic than other roll alloys
Service Information
You May Also Need
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
MECHANICAL PROPERTIES
| Flux | Classification | Hardness Rockwell C |
|---|---|---|
| Lincolnweld® 801® | Typical Result | 32-40 |
DEPOSIT COMPOSITION
| Flux | Classification | %C | %Cr | %Mn | %Mo | %Ni | %Si |
|---|---|---|---|---|---|---|---|
| Lincolnweld® 801® | Typical Result | 0.05 | 13.0 | 0.8 | 1.0 | 2.0 | 0.5 |
TYPICAL OPERATING PROCEDURES
| Diameter | Polarity |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
|---|---|---|---|---|
| 3/32 in (2.4 mm) | DC+ | 1.7 (65) | 24 | 250 |
| 3/32 in (2.4 mm) | DC+ | 3.0 (120) | 28 | 325 |
| 3/32 in (2.4 mm) | DC+ | 4.4 (175) | 31 | 425 |
| 1/8 in (3.2 mm) | DC+ | 1.5 (60) | 26 | 325 |
| 1/8 in (3.2 mm) | DC+ | 3.6 (140) | 30 | 575 |
| 5/32 in (4.0 mm) | DC+ | 1.4 (55) | 27 | 440 |
| 5/32 in (4.0 mm) | DC+ | 2.2 (85) | 30 | 575 |
| 5/32 in (4.0 mm) | DC+ | 2.9 (115) | 32 | 700 |