Lincolnweld® 781™ Submerged Arc (SAW) Flux

Soudage arc submergé | ED019587

700 Series Active Flux

Diamètre

Sélectionnez le diamètre

  • Flux

Emballage

Sélectionnez l'emballage

  • 50 lb Bag

DÉTAILS

  • Features fast follow characteristics that allow for uniform welds at high speeds without undercut or voids
  • Recommended for high speed, limited pass welding on clean plate and sheet steel
  • Good wetting action

Caractéristiques

  • Features fast follow characteristics that allow for uniform welds at high speeds without undercut or voids
  • Recommended for high speed, limited pass welding on clean plate and sheet steel
  • Good wetting action

Service d'information

Documentation

Vous pourriez avoir également besoin de

NA-5 Control

Coffret de commande NA-5

K356-2
NA-4 Control Box

Contrôleur NA-4

K388-2
LT-7 Tractor

Tracteur LT-7

K395-1
T4F SAE-500

Lincolnweld® 780® Submerged Arc (SAW) Flux

ED019586
Tout afficher

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. Page de recherche SDS

MECHANICAL PROPERTIES

Wire Classification Postweld Heat Treatment Yield Strength @ 0.2% Offset
MPa (ksi) 		Tensile Strength
MPa (ksi) 		Elongation
% 		Charpy V-Notch
J (ft-lbs) @ -20°C (0°F)
Lincolnweld® L-50® F7A0-EM13K-H8 As-welded 530 (76) 630 (92) 27 73 (54)
Lincolnweld® L-60 F7A0-EL12 As-welded 420 (60) 520 (75) 31 87 (64)
Lincolnweld® L-61® F7A0-EM12K As-welded 480 (70) 580 (84) 28 69 (51)
Lincolnweld® L-70 F9A0-EA1-G As-welded 570 (82) 650 (95) 26 56 (41)

DEPOSIT COMPOSITION

Wire Classification %C %Cr %Cu %Mn %Mo %Ni %P %S %Si Diffusible Hydrogen
mL/100g Weld Metal
Lincolnweld® L-50® F7A0-EM13K-H8 0.05 0.14 1.05 0.022 0.006 1.05 5
Lincolnweld® L-60 F7A0-EL12 0.06 0.11 1.04 0.017 0.008 0.73
Lincolnweld® L-61® F7A0-EM12K 0.04 0.06 1.52 0.020 0.008 0.97
Lincolnweld® L-70 F9A0-EA1-G 0.06 0.04 0.08 1.40 0.51 0.04 0.018 0.009 0.83

FLUX COMPOSITION

Classification %Al2O3 %CaF2 %CaO %MgO %MnO %Na2O %SiO2 %TiO2 %ZrO2 %Metal Alloys
Typical Result 4 5 1 13 15 2 26 10 19 3