33 lb Steel Spool Outershield MC-409 Flux-Cored Wire

Diameters / Packaging

Diameters
 11.3 KG SPOOL
1.1 mm ED031120
2.0 mm ED031122

Lincore® 55 Flux-Cored (FCAW-S) Wire

Flux-Cored Self-Shielded (FCAW-S) | ED031120

CLASSIFICATIONS:
EN ISO : T Fe2

LINCORE® 55 Wire for crane wheels, blower blades, rail ends, skip guides, cams, and transfer tables (Metal to Metal or Metal to Earth Abrasion).

Diameter

Select Diameter

  • 1.1 mm
  • 2.0 mm

Package

Select Package

  • 11.3 KG SPOOL

DETAILS

LINCORE® 55 produces a martensitic and some retained austenite deposit with a hardness range of Rockwell Hardness 50-59 (RHC) delivers a deposit which resists metal to-metal rolling or sliding wear as well as mild abrasion, offers unlimited layers with proper preheat and interpass temperatures and procedures.

Features

  • Delivers a deposit which resists metal-to-metal rolling or sliding wear as well as mild abrasion
  • To be used on carbon steel, low alloy steel and manganese steels
  • Unlimited layers with proper preheat and interpass temperatures and procedures

Service Information

Documentation

You May Also Need

33 lb Steel Spool Outershield MC-409 Flux-Cored Wire

Lincore® 55 Flux-Cored (FCAW-S) Wire

ED031122

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

MECHANICAL PROPERTIES

Classification Number of layer Hardness Rockwell C
Typical Result 1 Layer 50-59
Typical Result 2 Layers 50-60
Typical Result, Work-hardened 1 Layer 53-62
Typical Result, Work-hardened 2 Layers 56-62
Typical Result, Flame-hardened 2 Layers 52-54
Typical Result, 180°C (350°F) Interpass Temp 1 Layer 50-55
Typical Result, 180°C (350°F) Interpass Temp 2 Layers 55-59

DEPOSIT COMPOSITION

Classification Product Size %Al %C %Cr %Mn %Mo %P %S %Si
Typical Result .045" (1.1 mm) 1.4 0.45 5.3 1.3 0.8 0.010 0.004 0.53
Typical Result 1/16" (1.6 mm) 1.4 0.45 5.3 1.3 0.8 0.010 0.004 0.53
Typical Result 5/64" (2.0 mm) 1.4 0.45 5.3 1.4 0.8 0.010 0.004 0.60
Typical Result 7/64" (2.8 mm) 1.4 0.45 5.3 1.4 0.8 0.010 0.004 0.60

TYPICAL OPERATING PROCEDURES

Diameter Polarity ESO
mm (in.) 		Wire Feed Speed
m/min (in/min) 		Voltage
volts 		Approx. Current
amps 		Deposition Rate
kg/hr (lb/hr)
0.045 in (1.1 mm) DC+ 45 (1 3/4) 5.1 (200) 25 85 1.6 (3.6)
0.045 in (1.1 mm) DC+ 45 (1 3/4) 8.9 (350) 28 125 3.0 (6.6)
0.045 in (1.1 mm) DC+ 45 (1 3/4) 12.7 (500) 31 165 4.3 (9.4)
1/16 in (1.6 mm) DC+ 45 (1 3/4) 3.8 (150) 26 125 2.2 (4.8)
1/16 in (1.6 mm) DC+ 45 (1 3/4) 6.4 (250) 29 195 3.8 (8.4)
1/16 in (1.6 mm) DC+ 45 (1 3/4) 8.9 (350) 32 245 5.5 (12.1)
5/64 in (2.0 mm) DC+ 45 (1 3/4) 3.2 (125) 24 190 3.2 (7.0)
5/64 in (2.0 mm) DC+ 45 (1 3/4) 5.1 (200) 27 295 5.0 (11.0)
5/64 in (2.0 mm) DC+ 45 (1 3/4) 6.4 (250) 30 330 6.2 (13.7)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 2.3 (90) 25 280 3.8 (8.4)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 3.2 (125) 27 350 5.2 (11.5)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 4.4 (175) 30 420 7.3 (16.0)

NOTES

Note
Cold parts should be warmed to at least 25°C (75°F). Higher preheat of 150 - 260°C (300 - 500°F) may be necessary on thick parts or heavy sections.
Interpass temperatures between 150°C (300°F) and 200°C (400°F) do not affect the hardness of Lincore® 55 significantly.