DETAILS
LINCORE® 60-O ideal for carbon, low alloy, manganese, stainless steels and cast iron to be used at temperatures up to 704°C (1300°F) deposits feature higher alloy levels than to resist both abrasion and moderate impact limited to two layers with a Rockwell Hardness range of 55-60 (RHC) during sever abrasion.
Features
- Deposits feature higher alloy levels than to resist both abrasion and moderate impact
- Can be used at temperatures up to 704°C (1300°F)
- To be used on carbon, low alloy, manganese, stainless steels and cast iron
- Deposit is limited to two layers
Service Information
Documentation
You May Also Need
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
MECHANICAL PROPERTIES
| Classification | Number of layer | Hardness Rockwell C | Mass Loss (G65) |
|---|---|---|---|
| Typical Result | 1 Layer | 50-55 | 0.67 |
| Typical Result | 2 Layers | 55-58 | 0.20 |
DEPOSIT COMPOSITION
| Classification | Number of layer | %Al | %C | %Cr | %Mn | %Si |
|---|---|---|---|---|---|---|
| Typical Result | 2 Layers | 0.3-0.4 | 4.0-4.6 | 18.5-22.9 | 1.0-1.8 | 0.5-0.9 |
TYPICAL OPERATING PROCEDURES
| Diameter | Polarity |
ESO
mm (in.) |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
Deposition Rate
kg/hr (lb/hr) |
|---|---|---|---|---|---|---|
| .045" (1.1 mm) | DC+ | 19 (1) | 5.1 (200) | 21 | 125 | 1.9 (4.1) |
| .045" (1.1 mm) | DC+ | 19 (1) | 10.2 (400) | 25 | 185 | 3.7 (8.2) |
| .045" (1.1 mm) | DC+ | 19 (1) | 12.7 (500) | 27 | 210 | 4.7 (10.3) |
| 1/16" (1.6 mm) | DC+ | 22 (1) | 5.1 (200) | 28 | 240 | 3.4 (7.6) |
| 1/16" (1.6 mm) | DC+ | 22 (1) | 7.6 (300) | 31 | 300 | 5.1 (11.2) |
| 1/16" (1.6 mm) | DC+ | 22 (1) | 11.4 (450) | 33 | 350 | 7.5 (16.6) |
| 5/64" (2.0 mm) | DC+ | 32 (1) | 3.2 (125) | 26 | 250 | 3.4 (7.4) |
| 5/64" (2.0 mm) | DC+ | 32 (1) | 5.1 (200) | 30 | 350 | 5.4 (12.0) |
| 5/64" (2.0 mm) | DC+ | 32 (1) | 6.4 (250) | 32 | 400 | 6.8 (15.1) |
| 7/64" (2.8 mm) | DC+ | 29 (1) | 1.9 (75) | 27 | 250 | 3.4 (7.4) |
| 7/64" (2.8 mm) | DC+ | 29 (1) | 3.2 (125) | 30 | 340 | 5.4 (11.9) |
| 7/64" (2.8 mm) | DC+ | 29 (1) | 4.4 (175) | 32 | 420 | 7.5 (16.5) |
NOTES
| Note |
|---|
| Deposit thickness limit is two layers unless high travel speed is used to obtain very closely spaced check cracks. Many layers can be used with high travel speed and small bead sizes to ensure close-spaced check cracks. |
| Lincore® 60-O deposit cross cracks (commonly called cross-checking) on cooling. This is desirable, since cross-cracking of the deposit relieves cooling stresses and prevents spalling. |