DETAILS
This micro-alloyed MIG wire is designed for semi-automatic or automatic welding of root, hot, fill and cap passes on up to X80 grade pipe and root passes on up to X100 grade pipe.
Eigenschaften
- Wurzellage bis X100 sowie Hot Pass, Füll- und Decklage bis X80 Rohre
- Kerbschlagzähigkeit 69-95J bei-50°C
- Q2 Lot® - Zeugnis mit chemischer Analyse der Charge online verfügbar
- Idealer Drahtaustritt für Engspaltvorbereitungen
- ProTech® Verpackungssystem
Service Informationen
Dokumentation
Ergänzende Produkte
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS-Suchseite
CONFORMANCE
| CONFORMANCES | SPECIFICATION | CLASSIFICATION |
|---|---|---|
| AWS | AWS A5.28 | ER80S-G |
| ABS | ABS - Part 2 | 5YQ500SA H10 |
| CWB | AWS A5.28 | ER80S-G |
| DNV-GL | DNV - 2.9 | V Y50MS H5 |
| LR | LR - Chapter 11 | 5Y50S H5 |
| CONFORMANCES | SPECIFICATION | CLASSIFICATION |
|---|---|---|
| AWS | AWS A5.28 | ER80S-G |
| ABS | ABS - Part 2 | 5YQ500SA H10 |
| CWB | AWS A5.28 | ER80S-G |
| DNV-GL | DNV - 2.9 | V Y50MS H5 |
| LR | LR - Chapter 11 | 5Y50S H5 |
MECHANICAL PROPERTIES
| Classification | Shielding Gas | Polarity |
Yield Strength @ 0.2% Offset
MPa (ksi) |
Tensile Strength
MPa (ksi) |
Elongation
% |
Charpy V-Notch
J (ft-lbs) @ -30°C (-20°F) |
Charpy V-Notch
J (ft-lbs) @ -60°C (-75°F) |
Hardness Rockwell B |
|---|---|---|---|---|---|---|---|---|
| ER80S-G Requirement | Not Specified | DC+ | 550 (80) min. | Info. Only | ||||
| Typical Result, As-welded | 80% Ar, 20% CO2 | DC+ | 510-600 (74-87) | 620-670 (90-97) | 25-27 | 92-142 (68-105) | 68-100 (50-74) | 91-95 |
| Classification | Shielding Gas | Polarity |
Yield Strength @ 0.2% Offset
MPa (ksi) |
Tensile Strength
MPa (ksi) |
Elongation
% |
Charpy V-Notch
J (ft-lbs) @ -30°C (-20°F) |
Charpy V-Notch
J (ft-lbs) @ -60°C (-75°F) |
Hardness Rockwell B |
|---|---|---|---|---|---|---|---|---|
| ER80S-G Requirement | Not Specified | DC+ | 550 (80) min. | Info. Only | ||||
| Typical Result, As-welded | 80% Ar, 20% CO2 | DC+ | 510-600 (74-87) | 620-670 (90-97) | 25-27 | 92-142 (68-105) | 68-100 (50-74) | 91-95 |
DEPOSIT COMPOSITION
| Classification | Shielding Gas | Polarity | %C | %Cr | %Cu | %Mn | %Mo | %Ni | %P | %S | %Si | %Ti | %V | %Zr |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Typical Result | 80% Ar, 20% CO2 | DC+ | 0.06-0.09 | 0.03-0.05 | 0.16-0.20 | 1.27-1.32 | 0.02 max. | 0.75-0.87 | 0.005-0.009 | 0.005-0.009 | 0.56-0.65 | 0.03 | 0.005 max. | 0.001 max. |
| Classification | Shielding Gas | Polarity | %C | %Cr | %Cu | %Mn | %Mo | %Ni | %P | %S | %Si | %Ti | %V | %Zr |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Typical Result | 80% Ar, 20% CO2 | DC+ | 0.06-0.09 | 0.03-0.05 | 0.16-0.20 | 1.27-1.32 | 0.02 max. | 0.75-0.87 | 0.005-0.009 | 0.005-0.009 | 0.56-0.65 | 0.03 | 0.005 max. | 0.001 max. |
WIRE COMPOSITION
| Classification | %Al | %C | %Cr | %Mn | %Mo | %Ni | %P | %S | %Si | %Ti | %V | %Zr | %Ti+Zr | %Total Cu |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| ER80S-G Requirement | 0.30 min. * | 0.20 min. * | 0.50 min. * | |||||||||||
| Typical Result | 0.01 max. | 0.06-0.08 | 0.04 | 1.46-1.57 | 0.01 max. | 0.84-0.92 | 0.005-0.010 | 0.005-0.011 | 0.74-0.77 | 0.07 | 0.01 max. | 0.001 max. | 0.04-0.06 | 0.19-0.21 |
| Classification | %Al | %C | %Cr | %Mn | %Mo | %Ni | %P | %S | %Si | %Ti | %V | %Zr | %Ti+Zr | %Total Cu |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| ER80S-G Requirement | 0.30 min. * | 0.20 min. * | 0.50 min. * | |||||||||||
| Typical Result | 0.01 max. | 0.06-0.08 | 0.04 | 1.46-1.57 | 0.01 max. | 0.84-0.92 | 0.005-0.010 | 0.005-0.011 | 0.74-0.77 | 0.07 | 0.01 max. | 0.001 max. | 0.04-0.06 | 0.19-0.21 |
NOTES
| Note |
|---|
| * To meet the requirements of a "G" classification, the chemical composition of the eletrode must meet the minimum requirement for one or more of |