DETAILS
ULTRAMET B™316NF is ideal for Controlled carbon and niobium for optimum corrosion resistance and creep performance for typical application on Fabrication of fittings for minesweepers, Offshore industry – Downhole instrument collars, LPG & LNG storage vessels. Typical all weld metal measured with 0.2% offset. See test results disclaimer
Features
- Controlled carbon and niobium for optimum corrosion resistance and creep performance
- Designed to eliminate thermal fatigue and shock resistance at temperatures up to 1000°C (1832°F)
- Ideal for offshore industry – Downhole instrument collars
Disclaimers
Service Information
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
CONFORMANCE
CONFORMANCES | SPECIFICATION | CLASSIFICATION |
---|---|---|
AWS | AWS A5.29 | E81T1-Ni1M-JH4 |
AWS | AWS A5.36 | E81T1-M21A8-Ni1-H4, E81T1-M21P4-Ni1-H4 |
ABS | ABS - Part 2 | 4YQ460SA H5 |
CWB | CSA W48 | E551T1-M21A5-Ni1-H4 (E551T1-Ni1M-JH4) |
DNV-GL | DNV - 2.9 | IV Y46MS H5 |
LR | LR - Chapter 11 | 4Y46S H5 |
MECHANICAL PROPERTIES
Classification | Shielding Gas | Polarity |
Yield Strength @ 0.2% Offset
MPa (ksi) |
Tensile Strength
MPa (ksi) |
Elongation
% |
Charpy V-Notch
J (ft-lbs) @ -40°C (-40°F) |
Charpy V-Notch
J (ft-lbs) @ -50°C (-60°F) |
Charpy V-Notch
J (ft-lbs) @ -62°C (-80°F) |
---|---|---|---|---|---|---|---|---|
E81T1-Ni1M-JH4 Requirement | 75-80% Ar, balance CO2 | DC+ | 470 (68) min. | 550-690 (80-100) | 19 min. | 27 (20) min. | ||
E81T1-M21A8-Ni1-H4 Requirement | M21-ArC | DC+ | 470 (68) min. | 550-690 (80-100) | 19 min. | 27 (20) min. | ||
E81T1-M21P4-Ni1-H4 Requirement | M21-ArC | DC+ | 470 (68) min. | 550-690 (80-100) | 19 min. | 27 (20) min. | ||
Typical Result, As-welded | 75% Ar, 25% CO2 | DC+ | 480-610 (70-88) | 560-670 (82-96) | 20-29 | 92-123 (68-91) | 32-170 (24-125) | 37-41 (28-30) |
Typical Result, 1 hour @ 620°C (1150°F) | 75% Ar, 25% CO2 | DC+ | 470-510 (68-74) | 570-610 (83-88) | 26-29 | 56-148 (42-109) |
DEPOSIT COMPOSITION
Classification | Shielding Gas | Polarity | %B | %C | %Cr | %Mn | %Mo | %Ni | %P | %S | %Si | %V |
Diffusible Hydrogen
mL/100g Weld Metal |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
E81T1-Ni1M-JH4 Requirement | 75-80% Ar, balance CO2 | DC+ | 0.12 max. | 0.15 max. | 1.75 max. | 0.35 max. | 0.80 - 1.10 | 0.030 max. | 0.030 max. | 0.80 max. | 0.05 max. | 4 max. | |
E81T1-M21A8-Ni1-H4 Requirement | M21-ArC | DC+ | 0.12 max. | 0.15 max. | 1.75 max. | 0.35 max. | 0.80 - 1.10 | 0.030 max. | 0.030 max. | 0.80 max. | 0.05 max. | 4 max. | |
E81T1-M21P4-Ni1-H4 Requirement | M21-ArC | DC+ | 0.12 max. | 0.15 max. | 1.75 max. | 0.35 max. | 0.80 - 1.10 | 0.030 max. | 0.030 max. | 0.80 max. | 0.05 max. | 4 max. | |
Typical Result | 75% Ar, 25% CO2 | DC+ | 0.004-0.007 | 0.05-0.07 | 0.06 max. | 1.09-1.47 | 0.02 max. | 0.80-0.99 | 0.020 max. | 0.015 max. | 0.33-0.50 | 0.01 max. | 1.6-4 |
TYPICAL OPERATING PROCEDURES
Diameter | Shielding Gas | Polarity |
CTWD
mm (in.)⁽¹⁾ |
Wire Feed Speed
m/min (in/min) |
Voltage
volts |
Approx. Current
amps |
Melt-off Rate
kg/hr (lb/hr) |
Deposition Rate
kg/hr (lb/hr) |
Efficiency
% |
---|---|---|---|---|---|---|---|---|---|
0.045 in (1.1 mm) | 75% Ar, 25% CO2 | DC+ | 19 (3/4) | 4.4 (175) | 24 - 28 | 120 | 1.8 (3.9) | 1.5 (3.4) | 85-87 |
0.045 in (1.1 mm) | 75% Ar, 25% CO2 | DC+ | 19 (3/4) | 6.4 (250) | 25 - 29 | 140 | 2.5 (5.6) | 2.2 (4.8) | 85-87 |
0.045 in (1.1 mm) | 75% Ar, 25% CO2 | DC+ | 19 (3/4) | 7.6 (300) | 26 - 30 | 155 | 3.1 (6.8) | 2.6 (5.8) | 85-87 |
0.045 in (1.1 mm) | 75% Ar, 25% CO2 | DC+ | 19 (3/4) | 8.9 (350) | 27 - 31 | 170 | 3.6 (7.9) | 3.1 (6.8) | 85-87 |
0.045 in (1.1 mm) | 75% Ar, 25% CO2 | DC+ | 25 (1) | 10.2 (400) | 28 - 32 | 185 | 4.1 (9.0) | 3.5 (7.8) | 85-87 |
0.045 in (1.1 mm) | 75% Ar, 25% CO2 | DC+ | 25 (1) | 11.4 (450) | 28 - 32 | 200 | 4.6 (10.1) | 4.0 (8.8) | 85-87 |
0.045 in (1.1 mm) | 75% Ar, 25% CO2 | DC+ | 25 (1) | 12.7 (500) | 29 - 33 | 220 | 5.1 (11.3) | 4.4 (9.8) | 85-87 |
0.052 in (1.3 mm) | 75% Ar, 25% CO2 | DC+ | 19 (3/4) | 3.8 (150) | 24 - 28 | 150 | 2.1 (4.7) | 1.7 (3.8) | 81-84 |
0.052 in (1.3 mm) | 75% Ar, 25% CO2 | DC+ | 19 (3/4) | 5.1 (200) | 25 - 29 | 170 | 2.9 (6.3) | 2.4 (5.2) | 81-84 |
0.052 in (1.3 mm) | 75% Ar, 25% CO2 | DC+ | 19 (3/4) | 6.4 (250) | 26 - 30 | 195 | 3.5 (7.8) | 3.0 (6.5) | 81-84 |
0.052 in (1.3 mm) | 75% Ar, 25% CO2 | DC+ | 25 (1) | 7.6 (300) | 27 - 31 | 215 | 4.3 (9.4) | 3.6 (7.9) | 81-84 |
0.052 in (1.3 mm) | 75% Ar, 25% CO2 | DC+ | 25 (1) | 8.9 (350) | 28 - 32 | 240 | 5.0 (11.0) | 4.2 (9.2) | 81-84 |
1/16 in (1.6 mm) | 75% Ar, 25% CO2 | DC+ | 19 (3/4) | 3.8 (150) | 25 - 29 | 190 | 2.9 (6.4) | 2.4 (5.3) | 83-87 |
1/16 in (1.6 mm) | 75% Ar, 25% CO2 | DC+ | 19 (3/4) | 4.4 (175) | 25 - 29 | 205 | 3.4 (7.5) | 2.9 (6.3) | 83-87 |
1/16 in (1.6 mm) | 75% Ar, 25% CO2 | DC+ | 19 (3/4) | 5.1 (200) | 26 - 30 | 220 | 3.9 (8.5) | 3.3 (7.2) | 83-87 |
1/16 in (1.6 mm) | 75% Ar, 25% CO2 | DC+ | 19 (3/4) | 5.7 (225) | 26 - 30 | 230 | 4.4 (9.6) | 3.7 (8.1) | 83-87 |
1/16 in (1.6 mm) | 75% Ar, 25% CO2 | DC+ | 19 (3/4) | 6.4 (250) | 27 - 31 | 245 | 4.8 (10.6) | 4.1 (9.1) | 83-87 |
1/16 in (1.6 mm) | 75% Ar, 25% CO2 | DC+ | 25 (1) | 7.6 (300) | 27 - 31 | 275 | 5.8 (12.7) | 4.9 (10.9) | 83-87 |
1/16 in (1.6 mm) | 75% Ar, 25% CO2 | DC+ | 25 (1) | 8.3 (325) | 28 - 32 | 290 | 6.3 (13.8) | 5.4 (11.9) | 83-87 |
1/16 in (1.6 mm) | 75% Ar, 25% CO2 | DC+ | 25 (1) | 8.9 (350) | 28 - 32 | 300 | 6.7 (14.8) | 5.8 (12.8) | 83-87 |
NOTES
Note |
---|
⁽¹⁾ To estimate ESO subtract 1/4 in. (6.0 mm) from CTWD |