Diameters / Packaging
Diameters |
50 lb Carton |
---|---|
1/8 x 14 in (3.2 x 350 mm) | EDM13181414 |
3/16 x 14 in (4.8 x 350 mm) | EDM13181416 |
3/32 x 12 in (2.4 x 300 mm) | EDM13181403 |
5/32 x 14 in (4.0 x 350 mm) | EDM13181415 |
DETAILS
Features
- Good restrike characteristics
- Smooth and transfer and good wetting and low penetration
- Good deposition rates
Typical Applications
- Maintenance
- Repair
Welding Positions
- All
Shielding Gas
- Not Applicable
Special Features
- Specifically designed for vertical down welding of sheet metal and ornamental iron
Disclaimers
Service Information
Documentation
You May Also Need
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
CONFORMANCE
CONFORMANCES | SPECIFICATION | CLASSIFICATION |
---|---|---|
AWS | AWS A5.1 | E7014 |
MECHANICAL PROPERTIES
Classification |
Yield Strength @ 0.2% Offset
MPa (ksi) |
Tensile Strength
MPa (ksi) |
Elongation
% |
Hardness Rockwell B |
---|---|---|---|---|
E7014 Requirement | 400 (58) min. | 480 (70) min. | 17 min. | |
Typical Result, As-welded | 410-470 (60-69) | 490-540 (71-78) | 18-29 | 81-87 |
DEPOSIT COMPOSITION
Classification | %C | %Cr | %Mn | %Mo | %Ni | %P | %S | %Si | %V | %Mn+Ni+Cr+Mo+V |
---|---|---|---|---|---|---|---|---|---|---|
E7014 Requirement | 0.15 max. | 0.20 max. | 1.25 max. | 0.30 max. | 0.30 max. | 0.035 max. | 0.035 max. | 0.90 max. | 0.08 max. | 1.50 max. |
Typical Result | 0.05-0.08 | 0.02-0.04 | 0.44-0.67 | 0.01 max. | 0.01-0.04 | 0.010-0.018 | 0.007-0.012 | 0.16-0.47 | 0.01-0.02 | 0.49-0.74 |
TYPICAL OPERATING PROCEDURES
Diameter | Polarity⁽¹⁾ |
Current
Amps |
---|---|---|
3/32 in (2.4 mm) | AC | 80-100 |
3/32 in (2.4 mm) | DC± | 70-90 |
1/8 in (3.2 mm) | AC | 110-150 |
1/8 in (3.2 mm) | DC± | 100-140 |
5/32 in (4.0 mm) | AC | 140-190 |
5/32 in (4.0 mm) | DC± | 130-180 |
3/16 in (4.8 mm) | AC | 180-260 |
3/16 in (4.8 mm) | DC± | 160-240 |
NOTES
Note |
---|
⁽¹⁾ Preferred polarity is listed first. |