Lincore® 102HC

Alambre con núcleo metálico para proceso de Soldadura por Arco Sumergido (SAW) | ED026085

LINCORE® 102HC Metal-Cored Submerged Arc Wire designed for work rolls applications provides a higher hardness tool steel deposit during sliding wear (Metal to Metal)

Detalles

LINCORE® 102HC provides higher carbon compared to LINCORE® 102W for rebuilding, deposits hot weld above 204°C (400°F) machinable offers chromium, molybdenum and tungsten chemical composition to be used with recommended Lincoln weld® 802 and Lincoln weld® 802 for semiautomatic operations.

Características

  • Metal-cored wire with a higher carbon content than Lincore® 102W
  • Will give a higher hardness tool steel deposit
  • Deposit is “hot” [above 204°C (400°F)] machinable, for easy sizing after welding

Servicio de información

También puede necesitar

ANTES DE USARLO, LEA Y COMPRENDA LA HOJA DE DATOS DE SEGURIDAD (SDS) DE ESTE PRODUCTO Y LA INFORMACIÓN ESPECÍFICA IMPRESA EN EL ENVASE DEL PRODUCTO. Página de Búsqueda SDS

Ver los resultados de la prueba de limitación de responsabilidad

MECHANICAL PROPERTIES

Flux Classification Hardness Rockwell C
Lincolnweld® 802® Typical Result 54-60

DEPOSIT COMPOSITION

Flux Classification %C %Cr %Mn %Mo %Si %V %W
Lincolnweld® 802® Typical Result 0.40 6.7 2.1 1.6 1.6 0.20 1.3

TYPICAL OPERATING PROCEDURES

Diameter Polarity Wire Feed Speed
m/min (in/min)
Voltage
volts
Approx. Current
amps
3/32 in (2.4 mm) DC+ 1.7 (65) 24 240
3/32 in (2.4 mm) DC+ 3.0 (120) 28 400
3/32 in (2.4 mm) DC+ 4.4 (175) 31 500
1/8 in (3.2 mm) DC+ 1.5 (60) 26 390
1/8 in (3.2 mm) DC+ 2.5 (100) 28 540
1/8 in (3.2 mm) DC+ 3.6 (140) 30 680