50lb Coil Ultracore 70C

Diámetros / Embalaje

Diámetros
mm 		25 lb (11.3 kg) Steel Spool
 50 lb (22.7kg) Coil
0.045 in (1.1 mm) ED031128
1/16 in (1.6 mm) ED031129
5/64 in (2.0 mm) ED031130
7/64 in (2.8 mm) ED011164

Lincore® M

Soldadura Tubular Autoprotegida con Núcleo de Fundente (FCAW-S) | ED011164

CLASIFICACIONES:
EN/ISO : T Fe9

LINCORE® M Flux-Cored Self-Shielded Wire produces an austenitic manganese deposit on hammers, dredge parts, crushers, breaker bars and buckets applications. (Build Up and Joining)

Diámetro

Seleccionar diámetro

  • 0.045 in (1.1 mm)
  • 1/16 in (1.6 mm)
  • 5/64 in (2.0 mm)
  • 7/64 in (2.8 mm)

Paquete

Desencadenar

  • 50 lb (22.7kg) Coil

Detalles

LINCORE® M ideal for build-up and repair of Hadfield-type austenitic manganese materials as well as carbon and low alloy steels, deposits resistance on severe impact as well as moderate abrasion and offers unlimited layers with proper preheat and interpass temperatures and procedures.

Características

  • Deposit resists severe impact as well as moderate abrasion
  • Produces an austenitic manganese deposit that work-hardens
  • Recommended for build-up and repair of Hadfield-type austenitic manganese materials as well as carbon and low alloy steels
  • Unlimited layers with proper preheat and interpass temperatures and procedures

Servicio de información

También puede necesitar

33 lb Steel Spool Outershield MC-409 Flux-Cored Wire

Lincore® M

ED031128
33 lb Steel Spool Outershield MC-409 Flux-Cored Wire

Lincore® M

ED031129
33 lb Steel Spool Outershield MC-409 Flux-Cored Wire

Lincore® M

ED031130
SHADOW SPLIT LEATHER-SLEEVED JACKET

Chamarra para Soldador con Mangas de Carnaza Negra - K2986-L

K2986-L

ANTES DE USARLO, LEA Y COMPRENDA LA HOJA DE DATOS DE SEGURIDAD (SDS) DE ESTE PRODUCTO Y LA INFORMACIÓN ESPECÍFICA IMPRESA EN EL ENVASE DEL PRODUCTO. Página de Búsqueda SDS

Ver los resultados de la prueba de limitación de responsabilidad

MECHANICAL PROPERTIES

Classification Hardness Rockwell C
Typical Result 18-28
Typical Result, Work-hardened 30-48

DEPOSIT COMPOSITION

Classification %C %Cr %Mn %Ni %Si
Typical Result 0.6 4.9 13.0 0.5 0.4

TYPICAL OPERATING PROCEDURES

Diameter Polarity ESO
mm (in.) 		Wire Feed Speed
m/min (in/min) 		Voltage
volts 		Approx. Current
amps 		Deposition Rate
kg/hr (lb/hr)
0.045 in (1.1 mm) DC+ 25 (1) 5.1 (200) 22 80 1.5 (3.3)
0.045 in (1.1 mm) DC+ 25 (1) 8.9 (350) 24 145 2.7 (6.0)
0.045 in (1.1 mm) DC+ 25 (1) 12.7 (500) 26 185 4.4 (9.6)
1/16 in (1.6 mm) DC+ 30 (1 1/8) 3.8 (150) 23 130 2.2 (4.9)
1/16 in (1.6 mm) DC+ 30 (1 1/8) 6.4 (250) 25 200 3.9 (8.6)
1/16 in (1.6 mm) DC+ 30 (1 1/8) 8.9 (350) 27 250 5.6 (12.4)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 3.2 (125) 24 240 2.9 (6.4)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 4.4 (175) 27 300 4.2 (9.3)
5/64 in (2.0 mm) DC+ 32 (1 1/4) 6.4 (250) 29 360 6.2 (13.6)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 1.9 (75) 25 240 3.5 (7.8)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.2 (125) 27 360 6.2 (13.6)
7/64 in (2.8 mm) DC+ 45 (1 3/4) 3.8 (150) 28 395 7.5 (16.6)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 1.9 (75) 25 240 3.6 (8.0)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 4.4 (175) 30 400 8.8 (19.5)
7/64 in (2.8 mm) DC+ 64 (2 1/2) 5.7 (225) 32 455 11.6 (25.6)

NOTES

Note
As with all austenitic manganese welding products, interpass temperatures should be limited to 260°C (500°F) maximum.
A stringer bead, or at most, a slight weave is recommended to limit heat build-up. Excessive heat build-up causes manganese carbide precipitation that damages the toughness of austenitic manganese.