DETAILS
EXCALIBUR® 385-16 ideal for all weld metal for typical application on 904L Stainless Steels, Paper mill Equipment, Chemical process equipment used in fabrication of equipment, vessels for handling, storage of sulfuric acid and phosphoric acid. See test results disclaimer
Features
- The weld metal is fully austenitic
- Minimal heat input welding procedures should be used to avoid solidification cracking
- These materials are used in fabrication of equipment and vessels for handling and storage of sulfuric acid and phosphoric acid
Typical Applications
- Welding 904L Stainless Steels
- Paper mill Equipment
- Chemical process equipment
- Used in fabrication of equipment and vessels for handling and storage of sulfuric acid and phosphoric acid
Welding Positions
- All except vertical down
Shielding Gas
- N/A
Disclaimers
Service Information
Documentation
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
CONFORMANCE
CONFORMANCES | SPECIFICATION | CLASSIFICATION |
---|---|---|
AWS | AWS A5.4 | E385-16 |
MECHANICAL PROPERTIES
Classification |
Tensile Strength
MPa (ksi) |
Elongation
% |
---|---|---|
E385-16 Requirement | 520 (75) min. | 30 min. |
Typical Result, As-welded | 570-590 (83-86) | 40-41 |
DEPOSIT COMPOSITION
Classification | %C | %Cr | %Cu | %Mn | %Mo | %Ni | %P | %S | %Si |
---|---|---|---|---|---|---|---|---|---|
E385-16 Requirement | 0.03 max. | 19.5 - 21.5 | 1.2 - 2.0 | 1.0 - 2.5 | 4.2 - 5.2 | 24.0 - 26.0 | 0.03 max. | 0.02 max. | 0.90 max. |
Typical Result | 0.03 | 20.2 | 1.9 | 1.3 | 4.9 | 25.2 | 0.03 | 0.00 | 0.31 |
TYPICAL OPERATING PROCEDURES
Diameter | Polarity⁽¹⁾ |
Current
Amps |
---|---|---|
3/32 in (2.4 mm) | DC+ | 40-80 |
3/32 in (2.4 mm) | AC | 40-80 |
1/8 in (3.2 mm) | DC+ | 75-110 |
1/8 in (3.2 mm) | AC | 75-110 |
5/32 in (4.0 mm) | DC+ | 95-150 |
5/32 in (4.0 mm) | AC | 95-150 |
3/16 in (4.8 mm) | DC+ | 130-200 |
3/16 in (4.8 mm) | AC | 130-200 |
NOTES
Note |
---|
⁽¹⁾ Preferred polarity is listed first. |