Excalibur® 7018 XMR™

Stick (SMAW)

CLASSIFICATIONS:
E7018 H4R

Mild Steel, Low Hydrogen AWS E7018 H4R

Diameter

Select Diameter

  • 1/8 x 14 in (3.2 x 350 mm)
  • 3/32 x 14 in (2.4 x 350 mm)
  • 5/32 x 14 in (4.0 x 350 mm)

Package

Select Package

  • (3) 10 lb Easy Open Can
  • 50 lb Easy Open Can
Buy Now

DETAILS

Low hydrogen (or basic) electrodes are designed for applications susceptible to hydrogen cracking.

Features

  • Premium arc performance
  • Extreme bend ability
  • Excellent moisture resistance
  • Clean arc start
  • Clear puddle
  • Smooth arc

Typical Applications

  • Structural
  • Chemical processing structures
  • Pressure pipping
  • Ship building
  • Mild steel

Welding Positions

  • All except vertical down

Shielding Gas

  • Not Applicable

Special Features

  • Excalibur® 7018 XMR™ offers superior moisture resistance even after 24 hours – remaining below the moisture content limit for 15 hours more than required under AWS A5.

Disclaimers

Warning -

Cancer and Reproductive Harm -

www.P65Warnings.ca.gov

Service Information

Documentation

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

See test result disclaimer

CONFORMANCE

CONFORMANCES SPECIFICATION CLASSIFICATION
AWS AWS A5.1 E7018 H4R
ISO ISO 2560-B E4918 A H5
ABS ABS - Part 2 3YH5
BV BV - Chapter 5 3YHHH
CWB CSA W48 E4918
DNV-GL DNV - 2.9 3YH5
LR LR - Chapter 11 3YM H5

MECHANICAL PROPERTIES

Classification Yield Strength @ 0.2% Offset
MPa (ksi) 		Tensile Strength
MPa (ksi) 		Elongation
% 		Charpy V-Notch
J (ft-lbs) @ -30°C (-20°F) 		Hardness Rockwell B
E7018 H4R Requirement 400 (58) min. 480 (70) min. 22 min. 27 (20) min.
Typical Result, As-welded 420-470 (62-68) 520-570 (75-83) 27-32 96-416 (71-307) 82-89

DEPOSIT COMPOSITION

Classification %C %Cr %Mn %Mo %Ni %P %S %Si %V %Mn+Ni+Cr+Mo+V Diffusible Hydrogen
mL/100g Weld Metal 		1800F H2O - As received 1800F H2O - After 9 hrs at 80F/80%RH
E7018 H4R Requirement 0.15 max. 0.20 max. 1.60 max. 0.30 max. 0.30 max. 0.035 max. 0.035 max. 0.75 max. 0.08 max. 1.75 max. 4 max. 0.3 max. 0.4 max.
Typical Result 0.05-0.06 0.03 1.16-1.35 0.01 max. 0.02-0.03 0.010-0.014 0.005-0.009 0.43-0.54 0.01 max. 1.25-1.42 2 0.1 0.2

TYPICAL OPERATING PROCEDURES

Diameter Polarity Current
Amps
3/32" (2.4 mm) DC+ 70-110
3/32" (2.4 mm) AC 80-120
1/8" (3.2 mm) DC+ 90-160
1/8" (3.2 mm) AC 100-160
5/32" (4.0 mm) DC+ 130-210
5/32" (4.0 mm) AC 140-210