50 lb Can of Lincoln Electric Stick Electrodes

Diameters / Packaging

Diameters

Shield-Arc® 70+

Stick (SMAW)

CLASSIFICATIONS:
E8010-P1
E8010-G

Low Alloy, Cellulosic, Pipe • AWS E8010-G, Also meets E8010-P1

This product is not currently available for sale in this region.

DETAILS

Features

  • Light slag for minimal arc interference
  • Deep penetration
  • Clean, visible weld puddle
  • Superior puddle control

Typical Applications

  • Relatively high silicon pipe
  • API 5L X56 through X70 grade pipe
  • Cross country and in-plant pipe

Welding Positions

  • All positions

Shielding Gas

  • Not Applicable

Special Features

  • Recommend to switch to Pipeliner® Arc 80 for superior puddle control and visibility

Disclaimers

Warning -

Cancer and Reproductive Harm -

www.P65Warnings.ca.gov

You May Also Need

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

See test result disclaimer

CONFORMANCE

CONFORMANCES SPECIFICATION CLASSIFICATION
AWS AWS A5.5 E8010-G, E8010-P1
ISO ISO 2560-A E 46 4 1NiMo C 2 5
ABS AWS A5.5 E8010-G
CWB CSA W48 E5510-G

MECHANICAL PROPERTIES

Classification Yield Strength @ 0.2% Offset
MPa (ksi)
Tensile Strength
MPa (ksi)
Elongation
%
Charpy V-Notch
J (ft-lbs) @ -30°C (-20°F)
Charpy V-Notch
J (ft-lbs) @ -45°C (-50°F)
Hardness Rockwell B
E8010-G Requirement 460 (67) min. 550 (80) min. 19 min.
Typical Result, As-welded 470-570 (68-83) 570-660 (83-96) 20-26 57-89 (42-66) 32-68 (24-50) 87-95

DEPOSIT COMPOSITION

Classification %C %Cr %Cu %Mn %Mo %Nb %Ni %P %S %Si %V
E8010-G Requirement 0.30 min. * 1.00 min. * 0.20 min. * 0.50 min. * 0.03 max. 0.03 max. 0.80 min. * 0.10 min. *
Typical Result 0.13-0.17 0.13 max. 0.06 max. 0.55-0.95 0.10-0.42 0.010 max. 0.63-0.81 0.01-0.02 0.01 max. 0.06-0.16 0.005 max.

TYPICAL OPERATING PROCEDURES

Diameter Polarity Current
Amps
1/8 in (3.2 mm) DC+ 75-130
5/32 in (4.0 mm) DC+ 90-185
3/16 in (4.8 mm) DC+ 140-225

NOTES

Note
* To meet the requirements of a "G" classification, the chemical composition of the weld deposit must meet the minimum requirement for one or more of these elements.