Lincolnweld® 960

Soldadura por arco sumergido (SAW) | ED022412

Lincolnweld 960 es fundente de bajo costo de propósito general diseñado para soldar uniones a tope así como filetes de paso múltiple, recomendado para soldadura de arco sumergido automática y semiautomática, es un fundente versátil y rentable, que puede

Detalles

  • Low cost, general purpose flux designed to weld butt joints and both single and multiple pass fillets
  • Recommended for automatic and semiautomatic submerged arc welding
  • A versatile, cost-effective flux that can be used with many alloy systems
  • Can be used on A588 weathering steels when combined with Lincolnweld® LA-75

Características

  • Low cost, general purpose flux designed to weld butt joints and both single and multiple pass fillets
  • Recommended for automatic and semiautomatic submerged arc welding
  • A versatile, cost-effective flux that can be used with many alloy systems
  • Can be used on weathering steels when combined with Lincolnweld® LA-75
  • Actual (Type 3.1) certificates for each lot of flux showing chemical composition, particle size and moisture level are available in the certificate center of lincolnelectric.com
  • Q2 lot testing with mechanical results for ED030841

También puede necesitar

ANTES DE USARLO, LEA Y COMPRENDA LA HOJA DE DATOS DE SEGURIDAD (SDS) DE ESTE PRODUCTO Y LA INFORMACIÓN ESPECÍFICA IMPRESA EN EL ENVASE DEL PRODUCTO. Página de Búsqueda SDS

Ver los resultados de la prueba de limitación de responsabilidad

MECHANICAL PROPERTIES

Wire Classification Postweld Heat Treatment Yield Strength @ 0.2% Offset
MPa (ksi)
Tensile Strength
MPa (ksi)
Elongation
%
Charpy V-Notch
J (ft-lbs) @ -30°C (-20°F)
Charpy V-Notch
J (ft-lbs) @ -40°C (-40°F)
Charpy V-Notch
J (ft-lbs) @ -45°C (-50°F)
Charpy V-Notch
J (ft-lbs) @ -50°C (-60°F)
Lincolnweld® L-50® F7A2-EM13K-H4 As-welded 410 (59) 510 (74) 32 47 (35)
Lincolnweld® L-56® F7A2-EH11K-H4 As-welded 480 (69) 590 (86) 29 42 (31)
Lincolnweld® L-61® F6P4-EM12K 1 hour @ 620°C (1150°F) 340 (49) 460 (67) 35 140 (103)
Lincolnweld® L-61® F7A2-EM12K-H8 As-welded 410 (59) 500 (72) 31 152 (112)
Lincolnweld® LA-100 F10A4-EM2-G-H4 As-welded 650 (94) 720 (105) 23 50 (37)
Lincolnweld® LA-71 F7A2-EM14K-H4 As-welded 460 (67) 570 (82) 29 68 (50)
Lincolnweld® LA-71 F7P2-EM14K-H4 1 hour @ 620°C (1150°F) 410 (60) 540 (79) 30 94 (69)
Lincolnweld® LA-75 F7P6-ENi1K-Ni1-H4 1 hour @ 620°C (1150°F) 440 (64) 560 (81) 29 56 (41)
Lincolnweld® LA-75 F8A2-ENi1K-Ni1-H4 As-welded 480 (70) 580 (84) 25 81 (60)
Lincolnweld® LA-85 (LNS 165) F7P5-ENi5-G-H4 1 hour @ 620°C (1150°F) 470 (68) 570 (83) 27 58 (43)
Lincolnweld® LA-85 (LNS 165) F8A2-ENi5-G-H4 As-welded 500 (72) 590 (86) 26 68 (50)
Lincolnweld® LA-93 (LNS 151) F9P0-EB3-G-H8 1 hour @ 690°C (1275°F) 540 (79) 650 (94) 23

DEPOSIT COMPOSITION

Wire Classification %Ti %C %Cr %Cu %Mn %Mo %Ni %P %S %Si %Ti+V+Zr Diffusible Hydrogen
mL/100g Weld Metal
Lincolnweld® L-50® F7A2-EM13K-H4 0.06 0.09 1.48 0.016 0.008 0.58 4
Lincolnweld® L-56® F7A2-EH11K-H4 0.05 0.11 1.86 0.016 0.006 0.96 4
Lincolnweld® L-61® F6P4-EM12K 0.05 0.10 1.30 0.021 0.004 0.38
Lincolnweld® L-61® F7A2-EM12K-H8 0.05 0.06 1.27 0.015 0.009 0.42 5
Lincolnweld® LA-100 F10A4-EM2-G-H4 0.04 0.05 0.03 0.14 1.63 0.44 1.96 0.008 0.004 0.45 0.04 3
Lincolnweld® LA-71 F7A2-EM14K-H4 0.02 0.06 0.15 1.58 0.015 0.010 0.69 4
Lincolnweld® LA-71 F7P2-EM14K-H4 0.02 0.07 0.15 1.58 0.015 0.010 0.69 4
Lincolnweld® LA-75 F7P6-ENi1K-Ni1-H4 0.04 0.04 0.11 1.57 0.01 0.85 0.014 0.009 0.73 0.01 3
Lincolnweld® LA-75 F8A2-ENi1K-Ni1-H4 0.05 0.04 0.11 1.54 0.01 0.84 0.014 0.010 0.71 0.01 3
Lincolnweld® LA-85 (LNS 165) F7P5-ENi5-G-H4 0.05 0.03 0.09 1.61 0.22 0.85 0.016 0.010 0.42 4
Lincolnweld® LA-85 (LNS 165) F8A2-ENi5-G-H4 0.05 0.03 0.08 1.62 0.23 0.85 0.016 0.010 0.42 4
Lincolnweld® LA-93 (LNS 151) F9P0-EB3-G-H8 0.05 2.10 0.08 1.17 0.94 0.014 0.007 0.32 3

FLUX COMPOSITION

Classification %Al2O3 %CaF2 %CaO %MgO %MnO %Na2O %SiO2 %TiO2 %Metal Alloys
Typical Result 29 11 1 22 10 2 21 1 3