CHROMET® 2X

Stick (SMAW) | CHROMET2X-40-1

CLASSIFICATIONS:
E9018-B3 H4

B3 alloyed steel which meets specific requirements for improved temper embrittlement resistance with prolonged service at 400°C-600°C (752°F-1112°F)

Diameter

Select Diameter

  • 2.5 x 350 mm
  • 3/16 x 18 in (5.0 x 450 mm)
  • 3.2x350 mm
  • 4.0x450 mm

Package

Select Package

  • 16.8 kg Can
Buy Now

DETAILS

Low Alloy, Low Hydrogen • AWS A5.5 E9018-B3 H4

Features

  • B3 alloyed steel: 2.25% chromium, 1% molybdenum deposit which meets specific requirements for improved temper embrittlement resistance with prolonged service at 400°C-600°C (752°F-1112°F)
  • Excellent corrosion resistance in refineries to sulfur bearing crude oil at 250°C-450°C (482°F-842°F)
  • Moisture resistant coating provides low amounts of weld metal hydrogen levels for a superior weld
  • Weld metal chemistry is low in impurity elements allowing it to respect the X Factor (<15ppm) and J-factor (<120ppm)

Disclaimers

Warning -

Cancer and Reproductive Harm -

www.P65Warnings.ca.gov

Service Information

Documentation

BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page

See test result disclaimer

CONFORMANCE

CONFORMANCES SPECIFICATION CLASSIFICATION
AWS AWS A5.5 E9018-B3 H4R
ISO ISO 3580-A E CrMo2 B 3 2 H5
ISO ISO 3580-B E 6216-2C1M

MECHANICAL PROPERTIES

Classification Yield Strength @ 0.2% Offset
MPa (ksi) 		Tensile Strength
MPa (ksi) 		Elongation
%
E9018-B3 H4R Requirement 530 (77) min. 620 (90) min. 17 min.
E CrMo2 B 3 2 H5 Requirement 400 (58) min. 500 (72) min. 18 min.
E 6216-2C1M Requirement 530 (77) min. 620 (90) min. 15 min.
Typical Result, Stress relieved 570 (83) 670 (97) 22

DEPOSIT COMPOSITION

Classification %C %Cr %Mn %Mo %Nb %Ni %P %S %Si %Total Cu
E9018-B3 H4R Requirement 0.05 - 0.12 2.00 - 2.50 0.90 max. 0.90 - 1.20 0.03 max. 0.03 max. 0.80 max.
E CrMo2 B 3 2 H5 Requirement 0.05 - 0.12 2.0 - 2.6 0.40 - 1.30 0.90 - 1.30 0.01 max. 0.3 max. 0.030 max. 0.025 max. 0.80 max. 0.3 max.
E 6216-2C1M Requirement 0.05 - 0.12 2.0 - 2.6 0.40 - 1.30 0.90 - 1.30 0.030 max. 0.025 max. 0.80 max.
Typical Result 0.06 2.2 0.70 1.05 0.00 0.0 0.010 0.012 0.25 0.1 max.

TYPICAL OPERATING PROCEDURES

Diameter Current
Amps
2.5 mm (3/32") 70-110
3.2 mm (1/8") 80-140
4.0 mm (5/32") 100-180
5.0 mm 140-240