General purpose flux designed for butt and fillet welds joints, in both single and multiple pass techniques. Recommended for automatic and semi-automatic submerged arc welding. A versatile, cost-effective flux that can be used with many alloy systems.
Features
- Versatile flux
- High current carrying capacity
- For both single -run and multi-run techniques with moderate weld metal properties requirements
Disclaimers
Service Information
BEFORE USE, READ AND UNDERSTAND THE SAFETY DATA SHEET (SDS) FOR THIS PRODUCT AND SPECIFIC INFORMATION PRINTED ON THE PRODUCT CONTAINER. SDS Search page
See test result disclaimer
MECHANICAL PROPERTIES
| Wire | Classification | Postweld Heat Treatment |
Yield Strength @ 0.2% Offset
MPa (ksi) |
Tensile Strength
MPa (ksi) |
Elongation
% |
Charpy V-Notch
J (ft-lbs) @ -30°C (-20°F) |
Charpy V-Notch
J (ft-lbs) @ -40°C (-40°F) |
Charpy V-Notch
J (ft-lbs) @ -45°C (-50°F) |
Charpy V-Notch
J (ft-lbs) @ -50°C (-60°F) |
|---|---|---|---|---|---|---|---|---|---|
| Lincolnweld® L-50® | F7A2-EM13K-H4 | As-welded | 410 (59) | 510 (74) | 32 | 47 (35) | |||
| Lincolnweld® L-56® | F7A2-EH11K-H4 | As-welded | 480 (69) | 590 (86) | 29 | 42 (31) | |||
| Lincolnweld® L-61® | F6P4-EM12K | 1 hour @ 620°C (1150°F) | 340 (49) | 460 (67) | 35 | 140 (103) | |||
| Lincolnweld® L-61® | F7A2-EM12K-H8 | As-welded | 410 (59) | 500 (72) | 31 | 152 (112) | |||
| Lincolnweld® LA-100 | F10A4-EM2-G-H4 | As-welded | 650 (94) | 720 (105) | 23 | 50 (37) | |||
| Lincolnweld® LA-71 | F7A2-EM14K-H4 | As-welded | 460 (67) | 570 (82) | 29 | 68 (50) | |||
| Lincolnweld® LA-71 | F7P2-EM14K-H4 | 1 hour @ 620°C (1150°F) | 410 (60) | 540 (79) | 30 | 94 (69) | |||
| Lincolnweld® LA-75 | F7P6-ENi1K-Ni1-H4 | 1 hour @ 620°C (1150°F) | 440 (64) | 560 (81) | 29 | 56 (41) | |||
| Lincolnweld® LA-75 | F8A2-ENi1K-Ni1-H4 | As-welded | 480 (70) | 580 (84) | 25 | 81 (60) | |||
| Lincolnweld® LA-85 (LNS 165) | F7P5-ENi5-G-H4 | 1 hour @ 620°C (1150°F) | 470 (68) | 570 (83) | 27 | 58 (43) | |||
| Lincolnweld® LA-85 (LNS 165) | F8A2-ENi5-G-H4 | As-welded | 500 (72) | 590 (86) | 26 | 68 (50) | |||
| Lincolnweld® LA-93 (LNS 151) | F9P0-EB3-G-H8 | 1 hour @ 690°C (1275°F) | 540 (79) | 650 (94) | 23 |
DEPOSIT COMPOSITION
| Wire | Classification | %Ti | %C | %Cr | %Cu | %Mn | %Mo | %Ni | %P | %S | %Si | %Ti+V+Zr |
Diffusible Hydrogen
mL/100g Weld Metal |
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Lincolnweld® L-50® | F7A2-EM13K-H4 | 0.06 | 0.09 | 1.48 | 0.016 | 0.008 | 0.58 | 4 | |||||
| Lincolnweld® L-56® | F7A2-EH11K-H4 | 0.05 | 0.11 | 1.86 | 0.016 | 0.006 | 0.96 | 4 | |||||
| Lincolnweld® L-61® | F6P4-EM12K | 0.05 | 0.10 | 1.30 | 0.021 | 0.004 | 0.38 | ||||||
| Lincolnweld® L-61® | F7A2-EM12K-H8 | 0.05 | 0.06 | 1.27 | 0.015 | 0.009 | 0.42 | 5 | |||||
| Lincolnweld® LA-100 | F10A4-EM2-G-H4 | 0.04 | 0.05 | 0.03 | 0.14 | 1.63 | 0.44 | 1.96 | 0.008 | 0.004 | 0.45 | 0.04 | 3 |
| Lincolnweld® LA-71 | F7A2-EM14K-H4 | 0.02 | 0.06 | 0.15 | 1.58 | 0.015 | 0.010 | 0.69 | 4 | ||||
| Lincolnweld® LA-71 | F7P2-EM14K-H4 | 0.02 | 0.07 | 0.15 | 1.58 | 0.015 | 0.010 | 0.69 | 4 | ||||
| Lincolnweld® LA-75 | F7P6-ENi1K-Ni1-H4 | 0.04 | 0.04 | 0.11 | 1.57 | 0.01 | 0.85 | 0.014 | 0.009 | 0.73 | 0.01 | 3 | |
| Lincolnweld® LA-75 | F8A2-ENi1K-Ni1-H4 | 0.05 | 0.04 | 0.11 | 1.54 | 0.01 | 0.84 | 0.014 | 0.010 | 0.71 | 0.01 | 3 | |
| Lincolnweld® LA-85 (LNS 165) | F7P5-ENi5-G-H4 | 0.05 | 0.03 | 0.09 | 1.61 | 0.22 | 0.85 | 0.016 | 0.010 | 0.42 | 4 | ||
| Lincolnweld® LA-85 (LNS 165) | F8A2-ENi5-G-H4 | 0.05 | 0.03 | 0.08 | 1.62 | 0.23 | 0.85 | 0.016 | 0.010 | 0.42 | 4 | ||
| Lincolnweld® LA-93 (LNS 151) | F9P0-EB3-G-H8 | 0.05 | 2.10 | 0.08 | 1.17 | 0.94 | 0.014 | 0.007 | 0.32 | 3 |
FLUX COMPOSITION
| Classification | %Al2O3 | %CaF2 | %CaO | %MgO | %MnO | %Na2O | %SiO2 | %TiO2 | %Metal Alloys |
|---|---|---|---|---|---|---|---|---|---|
| Typical Result | 29 | 11 | 1 | 22 | 10 | 2 | 21 | 1 | 3 |